Austenitic SS 310 Sheets and Plates
Grade 310/310S or 310 stainless sheet is a medium carbon austenitic stainless steel, for high temperature applications. Alloy 310/310S is an austenitic stainless steel that combines excellent high temperature properties with good ductility and weldability.
Chemical Composition
|
GRADE |
NI |
Cr |
Si |
S |
MN |
C |
P |
Fe |
|
|---|---|---|---|---|---|---|---|---|---|
|
SS 310/310S |
MIN % |
19 |
24 |
– |
– |
– |
|||
|
MAX % |
22 |
26 |
1.5 |
0.03 |
2 |
0.25 |
0.045 |
BALANCE |
|
|
SS 310/310SS |
MIN % |
19 |
24 |
– |
– |
– |
|||
|
MAX % |
22 |
26 |
1.5 |
0.03 |
2 |
0.08 |
0.045 |
BALANCE |
310 grade stainless steel contains higher amounts of chromium and nickel content, making them highly resistant to oxidation and corrosion. Grade 310/310SS is a lower carbon version, less prone to embrittlement and sensitisation in service.
310 stainless steel plate and 310 stainless sheet is typically used for elevated temperature applications as its high chromium and nickel content provide solid corrosion resistance, excellent resistance to oxidation, and also has superior strength in temperatures up to 2100 Degree F.
Properties
Stainless Steel310/310S Sheets are very hard, wear resistant, tough, and inert to local overheating, and frequently engineered to particular service requirements. Stainless Steel310/310S Plates also have to be dimensionally stable during hardening and tempering.
Mechanical Properties
|
Grade |
Tensile Strength |
Yield Strength |
Elongation |
Hardness, MAX |
|
|---|---|---|---|---|---|
|
[MPA] |
[MPA] |
(% in 50mm) min |
HBW |
HRB |
|
|
SS 310/310S/310S |
515 |
205 |
40 |
217 |
95 |
The factor that SS 310/310S chemical composition has high chromium and nickel contents provides it comparable corrosion resistance, better resistance to oxidation and the retention of a larger fraction of room temperature ability than the common austenitic alloys like Type 304.
Physical Properties
|
Grade |
Density (g/cm3) |
Melting Range °C |
Elastic Modulus (GPa) |
Mean Co-eff of Thermal Expansion (μm/m/°C) |
Thermal Conductivity (W/m.K) |
Specific Heat (J/Kg.K) |
Electrical Resistivity (nΩ.m) |
||
|---|---|---|---|---|---|---|---|---|---|
|
0-100°C |
0-100°C |
0-315°C |
0-538°C |
at 100°C |
|||||
|
SS 310/310S/310S |
8 |
1400-1450 |
200 |
15.9 |
16.2 |
17 |
14.2 |
500 |
780 |
The stainless steel sheets and plates are generally stable while tempering and hardening. You can find it at various 310 stainless steel sheet suppliers. It can either have a coated, cold-formed or hot-formed surface. Stainless Steel310/310S/310S sheet and plates is an austenitic heat resistant alloy with excellent resistance to oxidation under mildly cyclic conditions through 2000°F.
Specification
The austenitic Stainless Steel310/310S sheet and plate or UNS S31000 specified by ASTM standard as ASTM A 240 or ASME SA-240 are readily available in different types such as, for example, SS 310/310S Plane sheet and Plate, Shim, Thin, Perforated, Polished, Diamond, Chequered, Hot rolled, Cold rolled, Annealed, Soft annealed , coils, clad plate, strip etc.
As per availability and requirement Alloy 310/310SSheets and Plate can be manufactured in different types but they also have different types of finishing on surface such as for example, Brushed ,Polished t, Mirror finish, Mirror polished, Hot rolled(HR), Cold rolled (CR), 2B,2D, BA NO(8), SATIN(Met with Plastic coated). The SS 310 plate price and SS 310 sheet price India is quite affordable so you can get it from various 310 stainless steel plate suppliers.
Application
Typical Applications of Stainless Steel310/310S Plates (UNS S31000) or 310 grade stainless steel is that they are used in fluidised bed combustors, kilns, radiant tubes, tube hangers for petroleum refining and steam boilers, coal gasifier internal components, lead pots, and more.
Alloy 310/310Sis used widely in industries such as heat treatment, chemical processing, Heat Exchangers, Oil Burner Parts, Furnace Parts, Refinery & Petrochemicals, LNG, Dairy, Oil & Gas, Chemical & Fertilizer etc.